Gd-Co nanosheet arrays coated on N-doped carbon spheres as cathode catalyst in photosynthetic microalgae microbial...

Biocompatible, durable and high catalytic cathode is crucial for the performance of photosynthetic microalgae microbial fuel cell (PMMFC). In this study, gadolinium-cobalt (Gd-Co) nanosheet arrays were coated on N-doped carbon spheres (N-CSs) that were supported using nickel foam (NF), to form a unique 3D hierarchical architecture of Gd-Co@N-CSs/NF cathode material. The morphology and structure of Gd-Co@N-CSs/NF was investigated by physicochemical characterization. The electricity generation and stability of NF, N-CSs/NF, Co@N-CSs/NF and Gd-Co@N-CSs/NF were evaluated using a dual-chamber PMMFC system with Chlorella vulgaris (C. vulgaris) in the cathode chamber. Results showed that doption of Gd to the cathode material resulted in Gd-Co@N-CSs/NF exhibiting superior catalytic activity for the oxygen reduction reaction (ORR), with an ORR peak potential of 0.78 V (vs. RHE). The electron transfer number (n) of Gd-Co@N-CSs/NF was 3.906, indicating ORR was mainly realized via 4e^- transfer pathway. Gd-Co@N-CSs/NF achieved a maximum power density of 115.9 mW m^-2 and an open circuit voltage of 614.8 mV, higher than the other three cathode materials. Gd-Co@N-CSs/NF exhibited excellent stability during 360 h of the PMMFC process, only dropping 5.8 % of maximum voltage. The cell density of C. vulgaris (3.7 × 10¹⁰ cells L^-1) in Gd-Co@N-CSs/NF system was significantly higher than those of NF, N-CSs/NF and Co@N-CSs/NF. This study shows that Gd-Co@N-CSs/NF is a promising cathode material and may be highly beneficial for the enhancement of PMMFC systems.