Shear bond strength of different luting agents to polyether ether ketone
Hossein Pourkhalili1, Hamid Neshandar Asli1, Newsha Toreihi2
1Department of Prosthodontics, Dental Sciences Research Center, School of Dentistry, Guilan University of Medical Sciences, Rasht, Iran.
Background:
Polyether ether ketone (PEEK) was recently introduced to dentistry. However, difficulty in provision of a strong durable bond is its main drawback. Thus, precise surface treatment and use of a suitable luting agent are imperative for bonding of PEEK restorations. This study aimed to assess the effect of type of luting agent on shear bond strength (SBS) of PEEK.
Materials And Methods:
In this in vitro study, 60 square-shaped PEEK samples were fabricated and sandblasted with 110 μm Al2O3 particles. The samples were then divided into four groups based on the type of cement used (n = 15): zinc phosphate cement, Panavia F2, Panavia V5, and resin-modified glass-ionomer (RMGI) cement. After bonding, the samples were thermocycled for 5000 cycles. The SBS was measured by a universal testing machine. The surface of samples was inspected under a video measuring machine to determine the mode of failure. Data were analyzed using the Kruskal-Wallis test via SPSS version 24 (α = 0.05).
And Methods:
In this in vitro study, 60 square-shaped PEEK samples were fabricated and sandblasted with 110 μm Al2O3 particles. The samples were then divided into four groups based on the type of cement used (n = 15): zinc phosphate cement, Panavia F2, Panavia V5, and resin-modified glass-ionomer (RMGI) cement. After bonding, the samples were thermocycled for 5000 cycles. The SBS was measured by a universal testing machine. The surface of samples was inspected under a video measuring machine to determine the mode of failure. Data were analyzed using the Kruskal-Wallis test via SPSS version 24 (α = 0.05).
Results:
RMGI did not bond to PEEK. The SBS values were 4.02 ± 2.87 megapascals (MPa) for Panavia V5, 10.84 ± 6.05 MPa for Panavia F2, and 10.50 ± 2.88 MPa for zinc phosphate. The SBS in the Panavia V5 group was significantly lower than that in the Panavia F2 (P = 0.001) and zinc phosphate (P < 0.001) groups. No significant difference existed between the Panavia F2 and zinc phosphate groups in this respect (P > 0.05).
Conclusion:
Panavia F2 resin cement and zinc phosphate conventional cement provided the highest bond strength to PEEK, while RMGI did not bond to PEEK.
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
01:14Polymer Classification: Architecture
00:43Complexometric Titration: Ligands
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...