Caries-inhibiting Effect of Microencapsulated Active Components in Pit and Fissure Sealants

The aim of the present in vitro study was to examine the caries-inhibiting effect of a pit and fissure sealant (PFS) containing ion-releasing microcapsules under cariogenic conditions in a biofilm artificial mouth.

Forty-eight human third molars were divided into four groups (n=12 per group). Fissures were extended with burs and sealed with experimental PFS. The four groups of specimens were treated as follows: 1) EPFS 1: EPFS (Premier Dental) of increasing viscosity, containing microcapsules loaded with remineralizing agents (calcium, phosphate, and fluoride ions); 2) US: fluoride-releasing PFS (UltraSeal XT plus, UltraDent Products, South Jordan, UT, USA); 3) EPFS 2: experimental PFS of constant viscosity containing microcapsules loaded with calcium, phosphate, and fluoride ions; and 4) FT: glass ionomer cement (GIC) (GC Fuji Triage CAPSULE WHITE glass ionomer cement, GC Europe NV, Leuven, Belgium). FT and US were used as control groups. EPFS 1 and EPFS 2 were the experimental groups. Specimens were stored in distilled water for 14 days at 37°C, subjected to 10,000 thermocycles (5°C and 55°C) and finally exposed to microbiological cycling in a Streptococcus mutans-based artificial mouth for 10 days. Replicas were made for scanning electron microscopic (SEM) evaluation and specimens were cut for fluorescence microscopy.

Overall demineralization depths at the margin of Fuji Triage were significantly shallower than in the other groups (p<0.05). Overall demineralization depths adjacent to the experimental pit and fissure sealant EPFS 2 (59±15 μm) were comparable to the values of the resin-based pit and fissure sealant UltraSeal XT plus (58±10 μm, p≥0.05). SEM revealed surface roughness of the GIC-based PFS.

The experimental PFS with microcapsules containing active components for remineralization did not show a caries-inhibiting effect compared to a fluoride-releasing resin-based PFS. Lower demineralization depths adjacent to GIC sealants indicate an anticariogenic effect through fluoride ion release.