In vitro evaluation of porous poly(hydroxybutyrate-co-hydroxyvalerate)/akermanite composite scaffolds manufactured...

Incorporation of a bioactive mineral filler in a biodegradable polyester scaffold is a promising strategy for scaffold assisted bone tissue engineering (TE). The current study evaluates the in vitro behavior of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV)/Akermanite (AKM) composite scaffolds manufactured using selective laser sintering (SLS). Exposure of the mineral filler on the surface of the scaffold skeleton was evident from in vitro mineralization in PBS. PHBV scaffolds and solvent cast films served as control samples and all materials showed preferential adsorption of fibronectin compared to serum albumin as well as non-cytotoxic response in human osteoblasts (hOB) at 24 h. hOB culture for up to 21 days revealed that the metabolic activity in PHBV films and scaffolds was significantly higher than that of PHBV/AKM scaffolds within the first two weeks of incubation. Afterwards, the metabolic activity in PHBV/AKM scaffolds exceeded that of the control samples. Confocal imaging showed cell penetration into the porous scaffolds. Significantly higher ALP activity was observed in PHBV/AKM scaffolds at all time points in both basal and osteogenic media. Mineralization during cell culture was observed on all samples with PHBV/AKM scaffolds exhibiting distinctly different mineral morphology. This study has demonstrated that the bioactivity of PHBV SLS scaffolds can be enhanced by incorporating AKM, making this an attractive candidate for bone TE application.