Dual structure engineering of SiO_x-acrylic yarn derived carbon nanofiber based foldable Si anodes for low-cost...

Silicon (Si) is attracted much attention due to its outstanding theoretical capacity (4200 mAh/g) as the anode of lithium-ion batteries (LIBs). However, the large volume change and low electron/ion conductivity during the charge and discharge process limit the electrochemical performance of Si-based anodes. Here we demonstrate a foldable acrylic yarn-based composite carbon nanofiber embedded by Si@SiO_x particles (Si@SiO_x-CACNFs) as the anode material. Since the amorphous SiO_x and carbon (C) coating on the outside of the Si particles can provide a double buffer for volume expansion while reducing the contact between the Si core and the electrolyte to form a thin and stable solid electrolyte interface (SEI) film. Simultaneous in-situ electrochemical impedance spectroscopy (in-situ EIS) and galvanostatic intermittent titration technique (GITT) tests show that SiO_x and C have higher ion/electron transport rates, and in addition, using acrylic fiber yarn and Zn(Ac)₂ as raw materials reduces the manufacturing cost and enhanced mechanical properties. Therefore, the half-cell can achieve a high initial Coulombic efficiency (ICE) of 82.3% and a reversible capacity of 1358.2 mAh/g after 180 cycles. It can return to its original shape and remain intact after four consecutive folds, and the soft-pack full battery can also light up LED lights under different bending conditions.