Effects of Rinsing Water Temperature and Preheated Composites on Microleakage of Composite Restorations with Two...

Objectives: The aim of this study was to evaluate the effects of rinsing water temperature and preheated composites on microleakage of class V restorations with two different bonding agents. Materials and Methods: Eighty class V cavities were prepared in the buccal and lingual surfaces of 40 molars. Single Bond and Prime and Bond NT bonding agents were used. The teeth were divided into four groups of 10. G₁: After acid etching, cavities were rinsed with 23^˚C water and filled with 23^˚C composite resin. G₂: Rinsing water and composite resin had 55^˚C temperature. G₃: Rinsing water had 55^˚C and composite resin had 23^˚C temperature. G₄: Rinsing water had 23^˚C and composite resin had 55^˚C temperature. The specimens were immersed in 0.5% basic fuchsine dye. Microleakage scores were analysed with the Kruskal-Wallis, Mann-Whitney U, and Wilcoxon tests. Results: There were significant differences in microleakage of specimens prepared with Single Bond and Prime and Bond NT only in group 1 (P<0.05). There were no significant differences between the microleakage of groups rinsed with different water temperatures (P>0.05). There were significant differences between the unheated and preheated composite groups (P<0.05). Conclusion: Preheating of composite is a valuable method to increase its adaptability and decrease microleakage of composite restorations.