Simultaneous stabilization/solidification of arsenic in acidic wastewater and tin mine tailings with synthetic...

Stabilization/Solidification (S/S) is considered as a feasible technology for the treatment of arsenic (As) in acidic wastewater (AW) and tin mine tailings (TMTs); however, high cost, high carbon footprint, and strict reaction conditions are the main limitations. Herein, a novel alkali-activated geopolymer material (AAGM) for S/S As was synthesized by combining AW, TMT, gypsum (GP), and metakaolin (MK). At room temperature, an initial As concentration of 3914 mg/L, a NaOH content of 4.98%, and an MK content of 20% decreased the As leaching concentration to 1.55 mg/L (<5 mg/L). The main S/S mechanisms of As included physical encapsulation of C-(A)-S-H and geopolymer structures, ion exchange of ettringite, and formation of Fe-As and Ca-As precipitates. Further studies showed that increasing initial As concentration and MK content facilitated the formation of Ca-As precipitates and C-(A)-S-H gels. The semi-dynamic leaching tests revealed that the leaching mechanism of As was surface wash-off. The effective diffusion coefficients of the samples were less than 10^-13 cm²/s, and the respective leachability indexes were greater than 9, indicating that AAGM was effective in preventing the leaching of As. Therefore, this study provides a green and low cost solution for the synergistic utilization of AW, TMT, GP, and MK.