Structural study and metal speciation assessments of waste PCBs and environmental implications: Outlooks for choosing
Farzane Vakilchap1, Seyyed Mohammad Mousavi2
1Biotechnology Group, Chemical Engineering Department, Tarbiat Modares University, Tehran, Iran.
Abstract:
Environmental protection from risks and disposal management of discarded mobile phone printed circuit boards (MPhPCBs) is a global issue. Although recycling is proposed as a solution, it is challenging to choose a sustainable method due to the insufficient recognition from extreme structural heterogeneity of these wastes based on their types. To this end, a thorough study on the structural characterization of PCBs using different analyses and metal speciation by sequential extraction procedure were performed. Understanding these information is an essential step in order to choose efficient methods to maximize selective recycling of metals and minimize environmental implications. PCBs were found to be potent metallic reservoirs after all metal content of PCBs were precisely measured. The structural analysis results of the sample included identification of different phases, functional groups, 45.1 % of the crystalline and 54.9 % of amorphous, the mesoporous nature (pore diameter mean ∼ 7.24 nm), hydrophobic property (contact angle ∼93.4°), the positive ζ-potential of particles at pH < (isoelectric point ∼5.4) and vice versa, and the particle size that were not oversized. The metal speciation outcome indicated over 80 % of the total content of elements such as Si, Sn, Ag, Au, Sr, Al, Cr, Nd, Ca, Ba, and P was in a solid crystal structure/residual fraction, which were hard recycled. The assessment of contamination levels of waste indicated the considerable contamination for the environment at global contamination factor ∼27.7, the moderate ecological risk at potential ecological risk assessment ∼82.9, and threats to public health. In addition, the metals of Pr, Mn, and Zn pose high risks because of their risk assessment code values of 42.7 %, 36.7 %, and 33.1 %, respectively. Leaching tests proved Waste Extraction Test was an aggressive method. ANC4 proposed high level of H+ consumption are required for metal leaching in future works.