Bond strength of three cements determined by centrifugal testing

Related Experiment Video

Updated: Sep 6, 2026

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior
11:07

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior

Published on: June 27, 2018

A H Arfaei, K Asgar

    The Journal of Prosthetic Dentistry
    |September 1, 1978
    PubMed

    More Related Videos

    Assessing Disaster Resilience of Concrete with Titanium Dioxide Nanoparticles05:45

    Assessing Disaster Resilience of Concrete with Titanium Dioxide Nanoparticles

    Published on: November 14, 2025

    Standardized Protocol to Evaluate the Effect of Surface Treatments, Luting Cements, and Thermocycling on PEEK–Composite Bond Strength04:23

    Standardized Protocol to Evaluate the Effect of Surface Treatments, Luting Cements, and Thermocycling on PEEK–Composite Bond Strength

    Published on: June 9, 2026

    Related Concept Videos

    Fineness of Cement01:15

    Fineness of Cement

    The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
    Direct...
    Soundness of Cement01:17

    Soundness of Cement

    The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
    Strength of Cement01:20

    Strength of Cement

    Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
    For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
    Bonding and Strength of Aggregate01:12

    Bonding and Strength of Aggregate

    The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
    Testing Water Quality01:14

    Testing Water Quality

    When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
    Tensile Strength Considerations of Concrete01:16

    Tensile Strength Considerations of Concrete

    Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
    The dimensions and shape of a concrete specimen also...