Preparation and characterization of micro/nanocellulose reinforced PVDF/wood composites

Polyvinylidene fluoride (PVDF) is commonly used in the chemical, electronic, and petrochemical industries because of its chemical and physical attributes. This study aimed to make novel PVDF-based composite with a high loading of silanized wood powder and micro/nanocellulose fibers, where glycerol acts as both a dispersant and a plasticizer all-in-one composite application for the first time. The purpose was also extended to systematically investigate their mechanical properties and melt flow. Results have demonstrated the efficiency of utilizing the cellulose fibers in bio-composites. With the addition of 30 wt% of filling materials, When the content of silanized cellulose fibers in glycerol dispersion is 25 wt%, the flexural strength and tensile strength reach the maximum value 72.30 MPa and 52.28 MPa. The experimental results indicate that silanized micro/nanocellulose fiber-reinforced PVDF/wood composites are a promising composite formula to help improve performance and reduce costs. It is an excellent example of utilizing biomass resources as a renewable/recyclable, sustainable and low-cost material to reduce the use of petroleum-based polymer, and improve the mechanical properties of composites.