The Mechanism of Wear Reduction in the Ni-CaF₂ Composite Material: Raman and Confocal Microscopy Insights

A powder metallurgy process was used to produce high temperature self-lubricating composites based on Ni, with varying content of calcium fluoride (10 wt.% and 20 wt.%). The wear properties of the samples were investigated by a pin-on-disc test at elevated temperature, up to 600 °C. Aside from standard techniques for the sample characterization, confocal microscopy and micro-Raman spectroscopy were used for the first time for this type of sample. These methods were used to examine the changes in topography and to detect the distribution of the tribofilm on sample surfaces. The addition of solid lubricant particles decreased the coefficient of friction and improved the tribological properties, because of the tribofilm which formed on sample surfaces.