Mechanical and Thermal Stress Analysis of Cervical Resin Composite Restorations Containing Different Ratios of Zinc...

Due to an increase in prevalence of cervical lesions, it is important to use appropriate restorative materials to reduce the incidence of secondary lesions. Owing to having antibacterial properties, cervical composite restorations containing different ratios of Zinc Oxide nanoparticles (ZnO NPs) have been analyzed using the Finite Element method to determine the optimal incorporation ratio from mechanical and thermal perspectives. A numerical simulation is conducted for a mandibular first premolar with a cervical lesion (1.5 × 2 × 3 mm³) restored with composites containing 0 to 5% wt. ZnO NPs. Subsequently, the samples are exposed to different thermo-mechanical boundary conditions, and stress distributions at different margins are examined. The accumulated stress in the restoration part increases for the 1% wt. sample, whereas the higher percentage of ZnO NPs leads to the reduction of stress values. In terms of different loading conditions, the least and most stress values in the restoration part are observed in central loading and lingually oblique force, respectively. The change in the surface temperature is inversely correlated with the ratio of ZnO NPs. In conclusion, the composite containing 5% wt. ZnO NPs showed the most proper thermo-mechanical behavior among all samples.