A Three-Dimensional Melamine Sponge Modified with MnOx Mixed Graphitic Carbon Nitride for Photothermal Catalysis of
Rongyang Yin1, Pengfei Sun1, Lujun Cheng1
1Department of Chemistry, Key Laboratory of Surface & Interface Science of Polymer Materials of Zhejiang Province, Zhejiang Sci-Tech University, 928 Second Avenue, Xiasha Higher Education Zone, Hangzhou 310018, China.
Abstract:
Much attention has been paid to developing effective visible light catalytic technologies for VOC oxidation without requiring extra energy. In this paper, a series of sponge-based catalysts with rich three-dimensional porosity are synthesized by combining MnOx and graphitic carbon nitride (GCN) with commercial melamine sponges (MS) coated with polydopamine (PDA), demonstrating excellent photothermal catalytic performance for formaldehyde (HCHO). The three-dimensional porous framework of MS can provide a good surface for material modification and a reliable interface for gas-solid interaction. The grown layer of PDA framework not only increases the near-infrared wavelength absorption for improving the light-to-heat conversion of catalysts, but also brings excellent adhesion for the subsequent addition of MnOX and GCN. The efficient formaldehyde oxidation is attributed to the sufficient oxygen vacancies generated by co-loaded MnOX and GCN, which is conducive to the activation of more O2- in the oxidation process. As the surface temperature of catalyst rapidly increases to its maximum value at ca. 115 °C under visible light irradiation, the HCHO concentration drops from 160 ppm to 46 ppm within 20 min. The reaction mechanism is certified as a classical Mars-van Krevelen mechanism based on the photo-induced thermal catalysis process.