Preparation of Novel Graphene/Silicone Rubber Nanocomposite Dielectric Foams

In order to obtain high dielectric silicone rubber (SR)-based nanocomposites, graphene (Gr) was added by ultrasonication and mechanical mixing for the preparation of a microporous structure. It was discovered that the Gr content and the expansion rate had a great impact on the cellular structure. Based on the effects of the Gr content and the expansion rate on the dielectric property, hybrid materials were prepared and better properties appeared, as expected. For all samples, the dielectric constant increased with the Gr content until 3 wt% and then decreased. When the Gr content was 3 wt% and the expansion rate was 2, the dielectric constant reached 18.14 (1 kHz), which was 55% higher than that of the non-expansion sample (11.74) and several times that of the pure sample (3~6). Meanwhile, the dielectric loss was less than 0.01. This work proposed a method for producing high dielectric materials with important applications in the field of capacitors, sensors, and micro-resistors.