Investigation on the Potential Use of Polypropylene Mesh for the Reinforcement of Heat-Polymerized PMMA Denture Base...

The aim of this study was to investigate the potential use of polypropylene (PP) hernia mesh as a reinforcement of PMMA denture base resin in comparison with metal and glass fiber meshes, with the expectation of enhancing the mechanical stability of the PMMA dentures in oral conditions. The control group with no mesh, the aluminum metal mesh (Al) group, the PP1 (PP mesh used on top) group, the PP2 (PP mesh used on both the top and bottom) group, the orthopedic casting tape with self-curing resin (DP0) group, and the flushed form (DPA) group were fabricated in a chromium mold. A total of 144 specimens were divided into three equal portions and subjected to: first, no treatment; second, thermal cycling only; and third, thermal cycling and chewing simulation. The flexural strength, maximum deformation, and flexural modulus were determined by a three-point bending test to compare mechanical properties. Fracture surfaces were evaluated by scanning electron microscopy. The obtained data were statistically analyzed by a two-way ANOVA test with Bonferroni corrections. The non-treated Al mesh reinforcement group exhibited the highest (82.66 ± 6.65 MPa) flexural strength, and the PP2 group treated with chewing simulation displayed the lowest (56.64 ± 4.59 MPa) flexural strength. The Al group showed the highest (7.25 ± 1.05 mm) maximum deformation and the PP2 group showed lowest (3.64 ± 0.28 mm) maximum deformation when both groups were not subjected to any treatment. The control group with no treatment exhibited the lowest (1556.98 ± 270.62 MPa) flexural modulus values, and the Al group with no treatment exhibited the highest (3106.07 ± 588.68 MPa) flexural modulus values. All the mesh groups displayed intact fractures. Any type of mesh used for reinforcement exhibited a significant change in all flexural properties (p < 0.001). The PP1 reinforcement group did not exhibit a significant change in mechanical properties when the effect of treatment was compared. Using PP hernia mesh on top enhanced the mechanical properties despite the weakening when it was used on both the top and bottom. The mechanical stability provided by the PP hernia mesh indicated it to be a promising candidate to be used for reinforcement.