Surface configuration of microarc oxidized Ti with regionally loaded chitosan hydrogel containing ciprofloxacin for...

The bacterial colonization and poor osseointegration of Ti implants significantly compromise their applications in load-bearing bone repair and replacement. To endorse the Ti with both excellent bioactivity and antibacterial ability, we developed a microarc oxidation coating that was modified uniformly by hydroxyapatite (HA) nanodots arrays and loaded regionally with chitosan hydrogel containing ciprofloxacin. The bonding between the HA nanodots covered coating and the chitosan hydrogel is further enhanced via silanization and chemical grafting of glutaraldehyde. Benefiting from the regionally loaded structure of the chitosan hydrogel, the chitosan hydrogel unloaded area can promote the cell adhesion and proliferation with excellent bioactivity, though relatively low OD value of cck8 has been observed at the beginning of the cell culturing. Whereas, the OD value of cck8 rises with the prolongation of the cell culturing time due to the degradation of the regionally loaded chitosan hydrogel. With the help of the laden ciprofloxacin in chitosan hydrogels, the sample effectively sterilizes the bacterial with a bacteriostatic ring. Therefore, regional loading of chitosan hydrogel containing ciprofloxacin on the modified microarc oxidation coating is a good approach to endorse Ti with both excellent bioactivity and antibacterial ability.