Yttrium- and Cerium-Codoped Ultrathin Metal-Organic Framework Nanosheet Arrays for High-Efficiency Electrocatalytic
Fajun Li1,2, Minghang Jiang1,3,4, Changgan Lai5
1MOE Key Laboratory of Mesoscopic Chemistry, MOE Key Laboratory of High Performance Polymer Materials and Technology, Jiangsu Key Laboratory of Advanced Organic Materials, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing, Jiangsu 210023, People's Republic of China.
Abstract:
The construction of low-cost, highly efficient, and stable electrocatalysts is a significant challenge for the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). Herein, we report a facile strategy to fabricate ultrathin metal-organic framework (MOF) nanosheet arrays doped with two rare-earth elements, Y and Ce, and self-supported on nickel foam (NF) to enhance the HER and OER performance by constructing abundant active sites and bimetallic synergistic effects. The NiYCe-MOF/NF features an ultrathin nanosheet array structure and is uniformly and richly codoped by Y and Ce. When it was explored as both the anode and cathode electrocatalysts for overall water splitting, it achieved 10 mA cm-2 at 136 and 245 mV for the HER and OER in an alkaline electrolyte, respectively. Notably, an extremely low cell voltage of 1.54 V was required to achieve 100 mA cm-2 in 1.0 M KOH solution, making it a promising substitute for noble-metal catalysts.
More Related Videos
07:13High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels
Published on: April 16, 2017
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021