Assessment of Caries-Affected Dentin Adhesive Interface Treated with Contemporary Conditioning Techniques

The aim of this study was to assess shear bond strength (SBS) and failure analysis of adhesion of composite resin (CR) to caries-affected dentin (CAD) pretreated with the Er,Cr:YSGG (ECY) laser, photodynamic therapy (PDT), and etch and rinse (ER) used for cavity disinfection. Methods used in this study included scanning electron microscopy (SEM), SBS analysis, failure analysis, and digital microscopy. The methods were adopted to assess bond integrity, CAD interface, smear layer, and hybridization. Thirty human third molars assessed clinically and having scores of 4 and 5 based on International Caries Detection and Assessment System (ICDAS) criteria were inspected. Infected dentin was removed. Dentin that was hard and stained pink was categorized as CAD. Ten samples were used in each group for pretreatment of CAD. Ten samples of healthy dentin [sound dentin (SD)] were collected separately and taken as controls. Samples were divided into the following groups: group 1: SD+ER; group 2: CAD+ER; group 3: CAD+ECY; and group 4: CAD+PDT after the pretreatment bonding agent was applied and the restorative procedure was performed using CR. CAD conditioned with PDT before bonding to CR demonstrated the lowest SBS values (11.22 ± 0.77 MPa), whereas the highest SBS values were observed in the SD surface treated with ER (18.25 ± 1.22 MPa). In CAD and SD pretreated with ER, majority of failure modes were cohesive failure and admixed failure, whereas in CAD pretreated with PDT and the ECY laser, the adhesive failure mode was pertinent. The use of the ECY laser and PDT on CAD for cavity disinfection does not have potential for application in clinical settings as it decreases bond integrity of CR. Moreover, the ER pretreatment method for CAD and SD remains the gold standard.