Copper-doped zeolitic imidazolate frameworks-8/hydroxyapatite composite coating endows magnesium alloy with excellent...

Magnesium (Mg) and its alloys exhibit an excellent prospect for orthopedic clinical application due to their outstanding biodegradability and mechanical adaptability. However, the rapid corrosion rate/latent device-associated infections may lead to a failed internal fixation of Mg-based implants. Herein, a novel composite coating consisted of outer copper-doped zeolitic imidazolate frameworks-8 and inner hydroxyapatite (Cu@ZIF-8/HA) was in situ constructed on AZ31B Mg alloy via a two-step approach of hydrothermal treatment and seeded solvothermal method. The results verified that the electrochemical impedance of the obtained Cu₄₅@ZIF-8/HA composite coating increased by two orders of magnitude to 6.6013 × 10⁴ Ω·cm² compared to that of bare Mg alloy. This was attributed to the reduced particle size of ZIF-8 nanoparticles due to the doped copper ions, which could be effectively grown in situ on the micro-nano flower-like structure of the HA-coated Mg alloy. Meanwhile, the Cu@ZIF-8/HA coating exhibited excellent antibacterial properties due to the release of copper ions and zinc ions from Cu@ZIF-8 dissolved in bacterial culture solution. The ICP results unraveled that the released concentration of copper and zinc ions could enhance the activity of alkaline phosphatase in the appropriate range during MC3T3-E1 cell culture in vitro for 7 days. This research revealed that the preparation of multifunctional metal-organic frameworks coating doped with antimicrobial metal ions via the seed layer solvothermal method was significant for studying the antimicrobial properties, osteogenic performance and corrosion resistance of Mg-based bioactive coatings.