Photocatalytic assessed adsorptive removal of tinidazole from aqueous environment using reduced magnetic graphene...

Antibiotics (tinidazole (TNZ)) in wastewater, exhibit adverse effects on humans and ecosystem. The current study was aimed to synthesize photocatalysts mrGO/BiOCl and mrGO/BiOCl/Ag. mrGO was coupled with BiOCl by hydrothermal method and Ag was deposited over it. The synthesized mrGO/BiOCl and mrGO/BiOCl/Ag were confirmed by Pzc analysis (5.5 and 4.4 for mrGO/BiOCl and mrGO/BiOCl/Ag, respectively), surface area analysis (380 m² g^-1, 227.7 m² g^-1, 220 m² g^-1 for mrGO, mrGO/BiOCl and mrGO/BiOCl/Ag respectively), elemental analysis (Ag, O, Bi, Fe), surface morphology (rough ball like sphere of mrGO/BiOCl and cubic Ag nanoparticles in mrGO/BiOCl/Ag), functional groups and band gap (Eg) determination. The Eg was determined using Kubelka-Munk equation as 3.5 and 2.8 eV for mrGO/BiOCl and mrGO/BiOCl/Ag respectively. During the adsorption study, the best experimental conditions for various operating parameters such as pH (2), contact time (5 min for mrGO/BiOCl and 10 min for mrGO/BiOCl/Ag under UV irradiation), TNZ concentration (18 μgL^-1) and catalyst dosage (0.001 g) were achieved. Kinetic study revealed that both composites followed pseudo second order kinetics (R² = 0.9979 and 0.9986, respectively). Data of rGO/BiOCl was fitted to Freundlich adsorption model (R² = 0.9687) and rGO/BiOCl/Ag fitted to Langmuir adsorption model (R² = 0.9994). Moreover, thermodynamic parameters confirmed that a photodegradation phenomenon was spontaneous and exothermic. The results confirmed that rGO/BiOCl and rGO/BiOCl/Ag are appropriate composites for TNZ removal from the aqueous environment with removal efficiency of 97 and 24%, respectively.