Surface defects and particle size determine transport of CdSe quantum dots out of plastics and into the environment

Polymers incorporating quantum dots (QDs) have attracted interest as components of next-generation consumer products, but there is uncertainty about how these potentially hazardous materials may impact human health and the environment. We investigated how the transport (migration) of QDs out of polymers and into the environment is linked to their size and surface characteristics. Cadmium selenide (CdSe) QDs with diameters ranging from 2.15 to 4.63 nm were incorporated into low-density polyethylene (LDPE). Photoluminescence was used as an indicator of QD surface defect density. Normalized migration of QDs into 3% acetic acid over 15 days ranged from 13.1 ± 0.6-452.5 ± 31.9 ng per cm² of polymer surface area. Migrated QD mass was negatively correlated to QD diameter and was also higher when QDs had photoluminescence consistent with larger surface defect densities. The results imply that migration is driven by oxidative degradation of QDs originating at surface defect sites and transport of oxidation products along concentration gradients. A semi-empirical framework was developed to model the migration data. The model supports this mechanism and suggests that QD surface reactivity also drives the relationship between QD size and migration, with specific surface area playing a less important role.