Environmentally friendly preparation of lignin/paraffin/epoxy resin composite-coated urea and evaluation for nitrogen...

Novel lignin/paraffin/epoxy resin composite coated urea (LPECCU) was successfully prepared. Paraffin and epoxy resin (ER) were used to improve the slow-release properties of the lignin-based polyurethane (LPU) coated urea. The relationships among the N release characteristics, liquid-solid rate, -CNO/-OH molar rate and film formation rate in the coating material of LPECCU were investigated. The results showed that the water contact angle (WCA) of the LPU-paraffin increased with the rate of liquid-solid rate (73.61-88.19°) and -CNO/-OH molar rate (65.17-82.24°) increased. The average particle hardness of LPECCU decreased with the increased of liquid-solid rate (57.10-66.80 N) and the reduced of -CNO/-OH molar rate (48.11-63.00 N). The LPECCU emerged compact micro-structure, low sustained release and high compressive resistance by adding paraffin and ER. The coating material of LPECCU appeared excellent biodegradability in the soil. The optimal N cumulative release rate (72.49 %) of LPECCU was obtained (liquid-solid rate of 1.43, -CNO/-OH molar rate of 2, and the film formation rate of 6.66 %). The lettuce growth study was conducted to further evaluate the pot application of the LPECCU. In comparison to conventional urea, LPECCU could improve the total dry matter accumulation and N use efficiency of the lettuce.