Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Fracture strength, pull-out bond strength, and volume of luting agent of tooth-colored CAD-CAM post-and-cores
Hiromi Saisho1, Gabriela Marcolina2, Fabricio Perucelli3
1Master's student, Graduate Program in Dentistry, School of Life Sciences, Pontifícia Universidade Católica do Paraná (PUCPR), Curitiba, PR, Brazil.
Statement Of Problem:
Little is known about the fracture strength, retention, and adaptation of post-and-cores fabricated with novel tooth-colored materials by computer-aided design and computer-aided manufacturing (CAD-CAM).
Purpose:
The purpose of this in vitro study was to investigate the fracture strength, pull-out bond strength (POBS), and volume of luting agent of endodontically treated premolars restored with post-and-cores milled from different CAD-CAM materials.
Material And Methods:
Post spaces were prepared in 80 human premolars in which post-and-cores fabricated with polyetheretherketone (PK; Ceramill PEEK), nanohybrid composite resin (BB; Brava Block), polymer-infiltrated ceramic (EN; VITA Enamic), and fiber-reinforced epoxy resin (GF; Fiber Cad Post & Core) CAD-CAM materials were luted (n=20). All specimens were subjected to thermal aging (3000 cycles at 5 °C and 55 °C with a 20-second dwell time). Half of the specimens were subjected to mechanical fatigue (250 000 cycles at 5 Hz) before fracture strength testing, while the other half was submitted to POBS testing and volume of luting agent measurement. Fracture strength data were analyzed by 1-way ANOVA, while POBS and volume of luting agent data were submitted to Kruskal-Wallis followed by the Bonferroni-Dunn multiple comparison tests. The correlation between POBS and the volume of luting agent was determined by the Spearman test (α=.05).
Results:
POBS of GF was significantly higher than that for PK (P<.001); however, failure load (P=.160) and volume of luting agent (P=.390) values did not differ. EN showed the highest percentage of catastrophic failures (20%), while PK exhibited only core deformations. POBS and cement film volume were not significantly correlated (P>.05).
Conclusions:
Different CAD-CAM materials did not influence the fracture strength and volume of luting agent of post-and-cores. Post-and-cores made with PEEK blocks showed lower bond strength to intracanal dentin than those made with fiber-reinforced epoxy resin blocks. No significant correlation was found between bond strength and the volume of luting agent.
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:17Mortar Properties
01:16Tensile Strength Considerations of Concrete
The dimensions and shape of a concrete specimen...
01:21Impact Strength of Concrete
01:27Fractures: Bone Repair
Minor fractures with no bone displacement are treated by immobilizing the fractured bone using a cast or splint. However, in the case of fractures with displaced bones, the broken bones are repositioned before immobilization to ensure successful healing without deformation and loss of function. The realignment of fractured bone ends is performed through a process called reduction. If the...