Ambient processed (110) preferred MAPbI₃ thin films for highly efficient perovskite solar cells

Organic-inorganic hybrid perovskites have attracted intensive attention due to their exceptional optoelectronic properties. With a massive leap of efficiency from 3.8% to 25.2% in a decade, perovskite solar cells (PSCs) have been considered the most promising next-generation photovoltaic technology. Recently, the methylamine (MA)-gas-mediated approach has been widely studied for preparing precursor solutions to deposit large scale perovskite thin films for PSCs. In this article, high-quality MAPbI₃ films were spin-coated using a MA-gas-mediated perovskite precursor. The deposited MAPbI₃ films showed larger crystal grains, lower surface roughness, and a preferred (110) crystal orientation compared to the films deposited by the Lewis adduct method. Planar PSC devices fabricated using the MA-gas-mediated precursor showed a high efficiency of 19.28% and a higher average efficiency than the devices fabricated by the Lewis adduct method.