An Influence of Oxygen Flow Rate and Spray Distance on the Porosity of HVOF Coating and Its Effects on Corrosion-A

Ali Raza1, Faiz Ahmad1, Thar M Badri1

  • 1Department of Mechanical Engineering, Universiti Teknologi PETRONAS, Seri Iskandar 32610, Perak, Malaysia.

Materials (Basel, Switzerland)
|September 23, 2022
PubMed

Keywords:
high-velocity oxyfuelhot corrosion sulfidationoxidationthermal spray coating

More Related Videos

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation07:44

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation

Published on: March 15, 2017

15.8K
Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media10:05

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media

Published on: November 3, 2018

18.0K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
211
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
376
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
248
General External Flow Characteristics01:26

General External Flow Characteristics

The study of external flow is essential for creating structures and objects that interact efficiently and safely with moving fluids, such as air or water. When a body is immersed in a flowing fluid, it experiences two primary forces: drag, which opposes motion along the flow direction, and lift, which acts perpendicular to the flow. The shape, size, and orientation of the object influence these forces.Streamlined and Blunt Bodies in External FlowObjects in fluid flow are classified as...
258
Factors Affecting Dissolution: Particle Size and Effective Surface Area01:23

Factors Affecting Dissolution: Particle Size and Effective Surface Area

Dissolution kinetics, an essential aspect of oral drug delivery, is significantly influenced by the drug's particle size. According to the Noyes-Whitney dissolution model, the dissolution rate correlates directly with the drug's surface area. The larger the surface area, the higher the drug's solubility in water, leading to a faster drug dissolution rate. Reducing particle size increases the effective surface area, enhancing the dissolution process. Micronization and nanosizing are...
967
Factors Affecting Activity Coefficient01:17

Factors Affecting Activity Coefficient

The extended Debye-Hückel equation indicates that the activity coefficient of an ion in an aqueous solution at 25°C depends on three partially interdependent properties: the ionic strength of the solution, the charge of the ion, and the ion size. 
The activity coefficient value for an ion is close to one when the solution has almost zero ionic strength, i.e., when the solution shows close to ideal behavior. As the ionic strength of the solution increases from 0 to 0.1 mol/L, a...
886