Synthesis and Characterization of Reproducible Linseed Oil-Loaded Silica Nanoparticles with Potential Use as Oxygen...

Commercially available oxygen scavengers used to prevent lipid autoxidation, microbial growth and enzymatic browning in food products present several issues, which include the usage of metals and their moisture dependence to work properly. We present the synthesis and characterization of a moisture-independent oil-based oxygen scavenging system comprised of linseed oil and silica nanoparticles. The system was synthesized via sol-gel chemistry and was characterized using morphological analysis (SEM, AFM, TEM, and N₂ adsorption/desorption), oil-loading analysis (TGA), and surface analysis (ζ-potential and ATR-FTIR). Performance of the system was evaluated through headspace measurements and reproducibility of synthetic procedure was verified using six replicates. Nanoparticles showed the desired spherical shape with a diameter of (122.7 ± 42.7 nm) and mesoporosity (pore diameter = 3.66 ± 0.08 nm), with an encapsulation efficiency of 33.9 ± 1.5% and a highly negative ζ-potential (-56.1 ± 1.2 mV) in basic solution. Performance of the system showed a promising high value for oxygen absorption of 25.8 ± 4.5 mL O₂/g of encapsulated oil (8.3 ± 1.5 mL O₂/g of nanocapsules) through a moisture independent mechanism, which suggests that the synthesized system can be used as an oxygen scavenger in dry atmosphere conditions.