Effect of vitrification on mechanical properties of porcine articular cartilage

Articular cartilage (AC) injuries do not heal primarily and large lesions progress to degenerative osteoarthritis. Osteochondral allograft transplantation is an effective surgical treatment but is limited by the lack of donor tissue availability. Fresh allografts can be stored hypothermically up to 28-45 days after which the tissue is no longer viable for transplantation. Vitrification is a method of cryopreservation with the potential to extend the storage time of AC. A specific protocol has been demonstrated to preserve high chondrocyte viability; however, its effect on various mechanical properties of the extracellular matrix (ECM) remains unknown and is the focus of this initial study. Porcine AC was subject to a defined vitrification protocol, using fresh and frozen samples as positive and negative controls, respectively; n = 20 for all three groups. Unconfined compression testing was used to assess mechanical properties of the tissue under rapid load, stress relaxation, and equilibrium conditions. The stress relaxation time constants (modeled with a 2-term Prony series) $$ and $$ were significantly lower for frozen (p = 0.014, p < 0.001) and vitrified (p = 0.009, p = 0.003) tissue compared to fresh, with no differences between frozen and vitrified samples (p = 0.848 and 0.105 for $$ and $$, respectively). These values indicate that frozen and vitrified samples relaxed more rapidly than fresh, which may suggest altered matrix composition and permeability post-treatment. These results represent the initial study in our experimental path to evaluate differences in mechanical properties of vitrified tissues.