Antimicrobial food packaging composite films prepared from hemicellulose/polyvinyl alcohol/potassium cinnamate blends

Hemicellulose and its derivatives have attracted extensive attention as packaging materials and various methods have been utilized to improve its film formation properties. To make use of the byproduct in dissolving pulp production, hemicellulose collected from waste water was modified by carboxymethylation and blended with polyvinyl alcohol (PVA) to prepare composite film by solution casting method. Potassium cinnamate (PC) was further incorporated to endow the film with antibacterial activity. The properties of the composite films were characterized. Due to the good compatibility and intermolecular interactions, the composite film exhibited moderate oxygen barrier property (3.64-12.21 cm³ μm m^-2 d^-1 KPa^-1). The flexibility of the film was improved compared with pure PVA film although tensile strength was decreased. The film had good UV barrier properties and good antibacterial properties due to the introduction of PC. GAB model could be used to predict moisture sorption of the composite films. Moreover, the obtained film showed good performance in cherry tomato preservation. This work provided a prospective route for utilization of hemicellulose recovered from waste water for high value-added products.