Regulating Surface Wettability and Charge Density of Porous Carbon Particles by In Situ Growth of Polyaniline for...

Both electrical conductivity and surface wettability are required for the selection of active carbon materials in flow-electrode capacitive deionization, while a trade-off exists between these two properties. In this work, a hybrid material with a thin layer of polyaniline (PANI) coating on activated carbon (AC/PANI) was successfully developed to retain excellent electrical conductivity and acquire good surface wettability. By adjusting the dosage of initiator, AC/PANI composites with different loading fractions of PANI were obtained. The electrochemical testing demonstrated that the AC/PANI composites have higher specific capacitance and lower ion diffusion resistance compared to pure AC, resulting in better desalinization performance. Specifically, with a feed concentration of 1600 mg/L, excellent adsorption capacity and high charge efficiency can be simultaneously achieved at 13.51 mg/g and 92.21%, respectively. Benefiting from the formation of a continuous electrical percolation network and reduced solid/liquid interfacial transport resistance, a 39% enhancement of average salt adsorption rate (from 0.54 to 0.75 μmol/min/cm²) was obtained.