Development of functional fillers as a self-healing system for dental resin composite
Andressa Goicochea Moreira1, Carlos Enrique Cuevas-Suárez2, Juliana Silva Ribeiro3
1Graduate Program in Dentistry, School of Dentistry, Federal University of Pelotas, Pelotas, Rio Grande do Sul, Brazil.
Objectives:
To evaluate the incorporation of repairing capsules containing different monomers and polymerization modulators on the self-healing efficiency of an experimental photopolymerizable resin-based composite.
Methods:
Self-healing capsules containing different monomers and polymerization modulators were prepared by emulsion polymerization: TCDHEPT (TEGDMA and DHEPT), BTCDHEPT (Bis-GMA, TEGDMA, and DHEPT), and BTCBPO (Bis-GMA, TEGDMA, and BPO). The capsules were analyzed through Fourier transform infrared spectroscopy and scanning electron microscopy. The capsules were added into experimental photopolymerizable resin composites establishing the following groups: ER (Control without capsules), ER+BPO, ER+BPO+TCDHEPT, and ER+BTCBPO+BTCDHEPT. Filtek Z350 resin composite (3 M ESPE) was used as a commercial reference. The materials were tested for degree of conversion (DC), flexural strength (σf), elastic modulus (Ef), fracture toughness (virgin KIC), self-healing efficiency (healed KIC), and roughness. For statistical analysis, the significance value was established at an a = 0.05 level.
Results:
When compared to the control material, the incorporation of repairing capsules did not affect DC, σf, and Ef. Fracture toughness was statistically similar between the experimental groups (p ≤ 0.05). Healed KIC was statistically different between the groups ER+TCDHEP and ER+BTCBPO+BTCDHEPT; the self-healing efficiency was higher for ER+TCDHEPT. Surface roughness was statistically similar among all groups.
Conclusions:
The use of self-healing capsules promoted repair of the material. Studies with material aging after the self-healing process are necessary to better demonstrate the effectiveness of this system.
Clinical Significance:
The self-healing system seemed to be a promising technology to be used in self-repaired restorative materials, which may prevent restoration fractures.