Phase Evolution and Electrochemical Properties of Nanometric Samarium Oxide for Stable Protonic Ceramic Fuel Cells

Electrochemical properties of metal oxide have a strong correlation with the crystalline structures. In this work, the effect of calcination temperature on the phase evolution and electrochemical properties of Sm₂ O₃ was systematically evaluated. The results demonstrate that the sample calcinated at 700 °C (SM-700) is composed of a pure cubic phase while it begins to convert into a monoclinic phase at a temperature above 800 °C and fully converts into a monoclinic phase at 1100 °C. Moreover, the evolution process causes atomic redistribution, and more oxygen vacancies are formed in cubic phase Sm₂ O₃ , contributing to the improved ionic conductivity. The ionic conductivity of 0.138 S cm^-1 and maximum power density of 895 mW cm^-2 at 520 °C are achieved using SM-700 as electrolyte for protonic ceramic fuel cell (PCFC). The cubic structure remains stable in the durability testing process and the SM-700 based fuel cell delivers enhanced stability of 140 mW cm^-2 for 100 h. This research develops a calcination evolution process to improve the ionic conductivity and fuel cell performance of the Sm₂ O₃ electrolyte for stable PCFC.