Spatial Relation Controllable Di-Defects Synergy Boosts Electrocatalytic Hydrogen Evolution Reaction over VSe₂...

Defect engineering of transition metal dichalcogenides (TMDCs) is important for improving electrocatalytic hydrogen evolution reaction (HER) performance. Herein, a facile and scalable atomic-level di-defect strategy over thermodynamically stable VSe₂ nanoflakes, yielding attractive improvements in the electrocatalytic HER performance over a wide electrolyte pH range is reported. The di-defect configuration with controllable spatial relation between single-atom (SA) V defects and single Se vacancy defects effectively triggers the electrocatalytic HER activity of the inert VSe₂ basal plane. When employed as a cathode, this di-defects decorated VSe₂ electrocatalyst requires overpotentials of 67.2, 72.3, and 122.3 mV to reach a HER current density of 10 mA cm^-2 under acidic, alkaline, and neutral conditions, respectively, which are superior to most previously reported non-noble metal HER electrocatalysts. Theoretical calculations reveal that the reactive microenvironment consists of two adjacent SA Mo atoms with two surrounding symmetric Se vacancies, yielding optimal water dissociation and hydrogen desorption kinetics. This study provides a scalable strategy for improving the electrocatalytic activity of other TMDCs with inert atoms in the basal plane.