Magnetic Zr-Based Metal-Organic Frameworks: A Highly Efficient Au (III) Trapper for Gold Recycling

In this work, the magnetic Zr-based MOF composites with excellent retrievability were prepared using Fe₃O₄@SiO₂ as the core and UiO-66-NH₂ as the shell. Fe₃O₄@SiO₂ core could introduce mesopores and result in capillary condensation in MOF composites, which aggravated with the dosage of Fe₃O₄@SiO₂. The as-synthesized MOF composites could be rapidly retrieved from aqueous solution via magnetic separation in 10 seconds. pH imposed an important effect on Au (III) adsorption by governing the ion exchange and electrostatic interaction between Au (III) anions and adsorbents, and the optimal adsorption happened at pH 7. The adsorption process fitted well with the pseudo-second order kinetics model and Langmuir adsorption model. The maximum adsorption capacity of Au (III) by FSUN-10 and FSUN-50 at 298 K were determined to be 611.18 mg∙g^-1 and 463.85 mg∙g^-1, respectively. Additionally, Au (III) uptakes increased with temperature. Beyond experiments, the adsorption mechanisms were thoroughly studied through systematic characterization, molecular dynamics simulation (MDS) and density functional theory (DFT) study. It was verified that Au (III) was adsorbed via coordination to hydroxyl and amino groups and was reduced to Au (I) and Au (0) by amino groups. The diffusion coefficient of Au (III) along UiO-66-NH₂ was calculated to be 5.8 × 10^-5 cm²∙s^-1. Moreover, the magnetic Zr-based MOF composites exhibit great industrial value in gold recycling with high adsorption selectivity and good recyclability.