The Effect of Welding Defects on the Long-Term Performance of HDPE Pipes

Huansheng Lai1,2, Dengshuai Fan3, Kanglin Liu3

  • 1Sino-French Institute of Nuclear Engineering and Technology, Sun Yat-sen University, Zhuhai 519082, China.

Polymers
|October 14, 2022
PubMed

Keywords:
HDPEbutt fusion jointcreep lifewelding defect

More Related Videos

Ultrasonic Welding of Thermoplastic Composite Coupons for Mechanical Characterization of Welded Joints through Single Lap Shear Testing08:40

Ultrasonic Welding of Thermoplastic Composite Coupons for Mechanical Characterization of Welded Joints through Single Lap Shear Testing

Published on: February 11, 2016

11.7K
Mechanical Expansion of Steel Tubing as a Solution to Leaky Wellbores09:32

Mechanical Expansion of Steel Tubing as a Solution to Leaky Wellbores

Published on: November 20, 2014

12.3K

Related Concept Videos

Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
268
Plastic Deformations01:19

Plastic Deformations

Plastic deformation represents a fundamental concept in materials science, which explains the irreversible change in the shape of a material when it experiences stress beyond its elastic capability. This phenomenon is important in structural engineering, especially in designing and analyzing cantilever beams—structures that are securely fixed at one end and bear loads at the opposite end. When these beams are subjected to loads within their elastic range, they will return to their...
172
Minor Losses in Pipes01:25

Minor Losses in Pipes

In pipe systems, minor losses refer to energy losses arising from components such as valves, bends, fittings, expansions, and other features that disrupt the steady flow of fluid. These disturbances cause energy dissipation through turbulence and resistance, which engineers quantify to manage system efficiency effectively.
Valves play a significant role in generating minor losses by obstructing or redirecting the fluid flow. When a valve is closed or partially closed, it restricts the flow...
1.2K
Bending of Material: Problem Solving01:09

Bending of Material: Problem Solving

In this lesson, determine the ratio of the maximum bending moments applied to two metal pipes, given that both pipes can withstand a maximum stress of 100 MPa. Both pipes have an outer radius of 1.8 cm. Pipe A has an inner radius of 1.5 cm, and Pipe B has an inner radius of 1 cm. The ratio of the maximum bending moment applied to two metallic pipes, each with a different inner and outer radius, is determined by considering their dimensions. The inner radius of the first pipe is 1.5 cm, and for...
233
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
226
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and...
250