The Effect of Oxalic Acid as the Pre-Activator for the Electropolishing of Additive Manufactured Titanium-Based...

The use of additive manufactured (AM) titanium-based materials has increased substantially for medical implants and aerospace components. However, the inferior surface roughness of additive manufactured products affects the outward appearance and reduces performance. This study determines whether activation treatment prior to electropolishing produces a better surface. Oxalic acid (OA) is used as a pre-activator using different experimental conditions and the surface roughness is reduced by electropolishing with an electrolyte of perchloric acid and glacial acetic acid. The SEM surface morphology, mechanical properties, phase transformation and electrochemical properties are measured to determine the effect of different degrees of roughness on the surface. The results show that the surface roughness of AM titanium-based samples decreases from 8.47 µm to 1.09 µm after activation using OA as a pre-treatment for electropolishing. After electropolishing using optimal parameters, the hardness and resistance to corrosion resistance are increased.