Influence of Aging and Surface Treatment on the Composite Bond Strength to Translucent 3Y-TZP Zirconia

The purpose of this study was to assess the effect of aging and alumina-particle air abrasion at different pressures on the bond strength of two luting composites to a translucent 3Y-TZP zirconia.

Half of the 192 disk-shaped zirconia specimens were aged in an autoclave (group A) for 20 h (134°C, 2 bar), and the other half was not aged (group N). For each group, a different surface treatment was applied: as-sintered (group SIN), alumina-particle air abrasion either at 1 bar (group 1B) or at 2.5 bar (group 2.5B). Disks were bonded to Plexiglas tubes filled with composite resin using a phosphate monomer-based luting composite (group SA) or with a separate phosphate monomer containing primer before using a phosphate-monomer-free luting composite (group V5). All specimens were subjected to tensile bond strength testing (TBS) before and after thermocycling.

There were no statistically significant differences caused by autoclave aging for the test groups before thermocycling, except for the A-SIN-SA group, where the TBS decreased significantly. The variation of the aluminaparticle air abrasion pressure showed no statistically significant effect, except in the N-1B-V5 group, where TBS was significantly lower than N-2.5B-V5. After thermocycling, the TBS of most groups decreased significantly. Specimens of the primer group, which were abraded at 1 bar, showed a significant decrease in TBS in comparison with alumina-particle air abrasion at 2.5 bar.

Twenty hours of autoclave aging had almost no influence on the bond strength of the test groups. For the primer/resin bonding system, higher pressure during alumina-particle air abrasion might help obtain a higher and more durable bond strength to zirconia.