Anti-passivation ability of sulfidated microscale zero valent iron and its application for 1,1,2,2-tetrachloroethane...

The performance of sulfidated zero valent iron (ZVI) for the degradation of chlorinated hydrocarbons under aerobic conditions remains unclear. In this study, sulfidated microscale ZVI (S-mZVI) was prepared for 1,1,2,2-tetrachloroethane (TeCA) degradation under aerobic conditions. Compared with mZVI, S-mZVI showed excellent passivation resistance during the degradation of TeCA and its hydrolysis/reduction products. This was probably because the existence of FeSx shell (FeS/FeS₂/FeS_n) protected the internal ZVI core from passivation. Though the outer layer of FeSx shell could be oxidized to FeS_n and Fe₂(SO₄)₃ as the reaction proceeded, the inner layer remained stable, which maintained the fast electron transfer capability of S-mZVI. The high temperature could enhance the degradation of TeCA, without compromising the anti-passivation and reusability of S-mZVI. Even after the fifth cycle, S-mZVI could still efficiently degrade 90% of TeCA within 24 h. Furthermore, it was found that the degradation of TeCA and its reduction products (e.g., dichloroethylene (DCE)) by S-mZVI relied on direct electron transfer and hydrogen radical (H•), respectively, which might explain the lower levels of toxic DCE in the S-mZVI system. This study provides valuable information for the practical application of S-mZVI in the treatment of wastewater containing halogenated hydrocarbons under ambient conditions.