Comprehensive characterization and environmental implications of spent telecommunication printed circuit boards:...

The management and prevention of environmental risks associated with spent telecommunications printed circuit boards (STPCBs) is a concerning issue worldwide. Recycling might be proposed as a proper method to overcome this issue. Despite knowing that, choosing a sustainable method is challenging because of STPCBs complexity. This problem was overcome by analyzing STPCBs using different analytical methods and metal speciation. Understanding these data is essential in selection strategies to maximize selective recycling of metals and to minimize environmental impact. This research focused on characterizing STPCBs based on their structural, morphological, physiochemical, surface, and thermal properties. The accurate measurement of metal contents, indicating 187,900 mg kg^-1 Cu, 22,540 mg kg^-1 Pb, 1320 mg kg^-1 Ag, and 205 mg kg^-1 Au elements, plus other base metals, revealed a remarkable potential value in STPCBs. The results of structural analyses indicated that the powder has a crystalline structure and consists of Cu, Sn and Pb phases as well as different functional groups. In addition, after evaluating the zeta potential of the sample, the isoelectric pH of the sample was observed to be 5.6, which indicates that the powder particles have a negative surface in an environment with a pH higher than this value. Further, the metal speciation via sequential extraction procedure was performed, which showed that a unique harsh recycling strategy is required due to the stable structure of STPCBs. According to the results of this analysis, the global contamination factor (GCF) value was 83.48, which indicates STPCBs have a high degree of contamination. Leaching tests and environmental criteria were also conducted on this waste. The findings suggest that STPCBs needs pretreatments before landfilling to lower the concentration of toxic metals. Also, waste extraction test was the most aggressive procedure to assess mobility. Achieving this information is considered an essential step to choosing the most efficient recycling methods that minimize environmental impact while maximizing selective recycling of metals.