Onset Potential for Electrolyte Oxidation and Ni-Rich Cathode Degradation in Lithium-Ion Batteries

High-capacity Ni-rich layered metal oxide cathodes are highly desirable to increase the energy density of lithium-ion batteries. However, these materials suffer from poor cycling performance, which is exacerbated by increased cell voltage. We demonstrate here the detrimental effect of ethylene carbonate (EC), a core component in conventional electrolytes, when NMC811 (LiNi_0.8Mn_0.1Co_0.1O₂) is charged above 4.4 V vs Li/Li⁺-the onset potential for lattice oxygen release. Oxygen loss is enhanced by EC-containing electrolytes-compared to EC-free-and correlates with more electrolyte oxidation/breakdown and cathode surface degradation, which increase concurrently above 4.4 V. In contrast, NMC111 (LiNi_0.33Mn_0.33Co_0.33O₂), which does not release oxygen up to 4.6 V, shows a similar extent of degradation irrespective of the electrolyte. This work highlights the incompatibility between conventional EC-based electrolytes and Ni-rich cathodes (more generally, cathodes that release lattice oxygen such as Li-/Mn-rich and disordered rocksalt cathodes) and motivates further work on wider classes of electrolytes and additives.