Effects of Different Titanium Surfaces Created by 3D Printing Methods, Particle Sizes, and Acid Etching on Protein...

The surfaces of 3D printed titanium prostheses have major impacts on the clinical performance of the prostheses. To investigate the surface effects of the products generated by 3D printed titanium on osseointegration, six surface types of titanium discs produced by the direct metal laser sintering (DMLS) and electron beam melting (EBM) methods, with two sizes of titanium particles and post-printing acid etching, were used to examine the surface topography and to explore the protein adsorption, pro-inflammatory cytokine gene expressions, and MC3T3-E1 cell adhesion, proliferation, and differentiation. The EBM-printed disc showed a stripy and smooth surface without evidence of the particles used, while the DMLS surface contained many particles. After acid etching, small particles on the DMLS surface were removed, whereas the large particles were left. Moreover, distinct proteins with low molecular weights were attached to the 3D printed titanium discs but not to the pre-printing titanium particles. The small titanium particles stimulated the highest TNF-α and IL-6 gene expressions at 24 h. The alizarin red content and osteocalcin gene expression at day 21 were the highest in the groups of acid-etched discs printed by DMLS with the small particles and by EBM. Therefore, the acid-treated surfaces without particles favor osteogenic differentiation. The surface design of 3D printed titanium prostheses should be based on their clinical applications.