Characteristics of Mortar Containing Oyster Shell as Fine Aggregate

In this study, oyster shells were processed and classified into sizes equal to or smaller than the fine aggregate threshold, and their engineering properties and fire-resistant performance were examined. The differences in heating weight loss of oyster shell aggregate (OSAs) with different particle sizes were examined using thermogravimetric analysis (TGA). The TGA results showed indicating that the temperature at which decarboxylation reaction started depended on the OSA particle size. The porosity of mortar specimens was analyzed using mercury intrusion porosimetry (MIP). The porosity area and porosity of the OSA-containing mortar increased with decreasing particle size. Mortar fire-resistant boards with heated for 2 h in accordance with the heating conditions of KS F 2257-1(methods of fire-resistant testing for structural element-general requirements) to measure their back-side temperature. The board made with OSA2.5 exhibited 273.2 °C, which is more than 90 °C higher than the back-side temperature of the board with OSA 0.6Under. Such difference was attributed to the greater heat transfer delay caused by higher porosity, porosity area, and specific surface area in OSAs with small particle sizes. The TGA results combined with the heating test results suggested that CO₂ would be generated at different temperatures in boards containing OSAs with different particle sizes because of the differences in the endothermic reaction temperature.