NiB-CrC Coatings Prepared by Magnetron Sputtering Using Composite Ceramic NiCr-BC Target Produced by Detonation Spray...

A metal-ceramic composite target for magnetron sputtering was fabricated for the first time by a robotic complex for the detonation spraying of coatings equipped with a multi-chamber detonation accelerator. A mixture of metal and ceramic NiCr/B₄C powders was sprayed onto the copper base of the cylindrical composite target cathode. The study of the structure of a metal-ceramic composite coating target using scanning electron microscopy showed that the coating material is dense without visible pores; the elemental composition is evenly distributed in the material. The study of the cathode sputtering area after deposition in the DC mode showed that there are uniform traces of annular erosion on the target surface. The obtained cathode target with an NiCr-70B₄C coating was used to deposit the NiB-Cr₇C₃ coating on flat specimens of 65G steel using equipment for magnetron sputtering UNICOAT 200. The coating was applied in the Direct Current mode. A dense NiB-Cr₇C₃ coating with a thickness of 2 μm was obtained. The NiB-Cr₇C₃ coating has a quasi-amorphous structure. The microstructures and concentration of oxygen and carbon impurities throughout the entire thickness of the coating were investigated by means of transmission electron microscopy. The results of the study show that the coatings have a nanocrystalline multi-phase structure. The microhardness of the NiB-Cr₇C₃ coating reached 10 GPa, and the adhesion fracture load exceeded 16 N. The results will open up new prospects for the further elaboration of technology for obtaining original composite cathodes for magnetron sputtering using detonation spraying of coatings.