Liquid Oxygen Compatibility and Ultra-Low-Temperature Mechanical Properties of Modified epoxy Resin Containing...

Endowing epoxy resin (EP) with prospective liquid oxygen compatibility (LOC) as well as enhanced ultra-low-temperature mechanical properties is urgently required in order to broaden its applications in aerospace engineering. In this study, a reactive phosphorus/nitrogen-containing aromatic ethylenediamine (BSEA) was introduced as a reactive component to enhance the LOC and ultra-low-temperature mechanical properties of an EP/biscitraconimide resin (BCI) system. The resultant EP thermosets showed no sensitivity reactions in the 98J liquid oxygen impact test (LOT) when the BSEA content reached 4 wt% or 5 wt%, indicating that they were compatible with liquid oxygen. Moreover, the bending properties, fracture toughness and impact strength of BSEA-modified EP were greatly enhanced at RT and cryogenic temperatures (77 K) at an appropriate level of BSEA content. The bending strength (251.64 MPa) increased by 113.67%, the fracture toughness (2.97 MPa·m^1/2) increased by 81.10%, and the impact strength (31.85 kJ·m^-2) increased by 128.81% compared with that of pure EP at 77 K. All the above results demonstrate that the BSEA exhibits broad application potential in liquid oxygen tanks and in the cryogenic field.