Micro-polluted water resources treatment by PVDF-TiO2 membrane combined with Fe2+/sodium dithionite (DTN)/O2
Wanying Xie1, Wei Song2, Ji Li3
1State Key Laboratory of Urban Water Resource and Environment, Shenzhen Key Laboratory of Water Resource Utilization and Environmental Pollution Control, Harbin Institute of Technology Shenzhen, Guangdong, 518055, PR China; College of Civil Engineering and Architecture, Xinjiang University, Urumqi, Xinjiang, 830017, PR China.
Abstract:
Modifying PVDF membrane by blending hydrophilic nano TiO2 has been highly concerning, but its practical application is not well investigated. In this study, PVDF-TiO2 membrane was employed in two modes to treat micro-polluted raw water for the first time, direct membrane filtration and pre-oxidation assists membrane filtration. At two filtration modes, the PVDF-TiO2 membrane had comparable rejection capability to the unmodified PVDF membrane, as the removal of permanganate index (CODMn) was 0.26-0.72 mg/L, UV254 was 0.0070-0.0618 cm-1, turbidity was 1.60-4.49 NTU, and the total number of colonies was 360-23,780 CFU/mL. As for raw water treatment, using Fe2+/sodium dithionite (DTN)/O2 system as the pre-oxidation process to assist the filtration of the PVDF-TiO2 membrane was feasible. After optimization, the applicable conditions of the Fe2+/DTN/O2 process were DTN dosage at 100 mg/L and a CFe/CDTN of 1:4. As a result, the effluent qualities of the PVDF-TiO2 membrane significantly improved. It was investigated that atrazine (ATZ), CODMn, UV254, and turbidity reduced, which was realized by the synergic effects of the pre-oxidation by free radicals and flocculation by iron. Pre-oxidation of the Fe2+/DTN/O2 process could also enhance the permeability of the PVDF-TiO2 membrane from 53.6 to 58.0 L/(m2·h), nearly two times the PVDF membrane. Besides, the practical fouling of the PVDF-TiO2 membrane was stably alleviated by the reduced Rt, Rre, and Rir, mainly due to constraining the internal pore fouling effectively.