Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in CuIn,GaSe2 Thin-film Solar Cells
Published on: July 19, 2019
Engineering the synthesized colloidal CuInS2 passivation layer in interface modification for CdS/CdSe quantum dot
Zhijun Liang1, Yifan Chen2, Rui Zhang1
1Institute of Physical Chemistry, College of Chemistry, Jilin University, Changchun 130012, P. R. China. xietf@jlu.edu.cn.
Abstract:
Interface modification is an important means to enhance the photovoltaic performance of quantum dot sensitized solar cells (QDSCs). The TiO2/CdS/CdSe solar cells are sensitized with CdS QDs and CdSe QDs, which inevitably introduces a new interface to form a recombination center. Therefore, it is necessary to coat a passivation layer in order to effectively inhibit charge recombination at the CdS/CdSe interface. In this work, CuInS2 (CIS) has been introduced into the CdS/CdSe QD system as an inner passivation layer and the CdS/CIS/CdSe photoanode structure has been fabricated in an environmentally friendly manner. The extracted charge amount (Q) is used to express the charge separation efficiency, indicating that we have obtained outstanding charge extraction efficiency in CIS based CdS/CdSe QDSCs. As a result, the photocurrent density of the TiO2/CdS/CIS/CdSe photoanode significantly has increased from 19.01 mA cm-2 to 22.74 mA cm-2 (TiO2/CdS/CdSe photoanode), which demonstrates a higher photoconversion efficiency of 4.52% in comparison with that of TiO2/CdS/CdSe photoanode.