The passivity breakdown of zinc antimony alloy as an anode in the alkaline batteries

Zn is utilized as an anode in alkaline batteries because of its propensity to produce a passive colloidal layer on its surface. Then the surface should be reactivated in the passive region. Therefore, the passive state on the surface can be significantly hindered by utilizing a tiny percentage of Sb alloyed with Zn. Accordingly, the effect of minor Sb alloying with Zn on the performance of anodic dissolution and passivation in concentrated alkaline media (6 M KOH, which is used in the batteries) was studied using potentiodynamic and potentiostatic techniques. Besides, the passive layers formed at various anodic potentials were characterized utilizing scanning electron microscopy (SEM) and X-ray diffraction (XRD). The data of potentiodynamic measurements exhibited the active-passive transition curve of all studied specimens. All obtained results revealed that passivation is gradually hindered with increasing Sb content in the alloy, and less passivity was obtained at 1% Sb. Along this, a dramatic rise in current density at a particular positive potential (+ 2.0 V vs. SCE) to markedly higher values only of the electrodes containing Sb is observed.