Analysis on mechanical properties and mesoscopic acoustic emission characteristics of prefabricated fracture cemented...

The mechanical characteristics of cemented paste backfill (CPB) are significantly influenced by the loading rate (LR) and initial defects. Therefore, the CPB with prefabricated fracture (PF, PFCPB) was prepared, and uniaxial compressive strength (UCS) tests considering LR and acoustic emission (AE) monitoring were performed. The particle flow code (PFC2D) was introduced to analyze the mesoscopic crack evolution of the filling body, and the moment tensor theory was used to invert the AE signals characteristics. The results show that as the PF angle increased, the UCS and elastic modulus (EM) of PFCPB decreased and then increased, and the 30° PF was the turning point. The mechanical properties of PFCPB were deteriorated by the presence of PF. Meanwhile, the mechanical properties of PFCPB were positively correlated with the LR. The stress-strain curve of PFCB (excluding 90°) showed bimodal curves. After the UCS test, the macro crack of PFCPB sprouted at the tip of PF or converged toward PF. PFCPB mainly suffered from shear failure, accompanied by a few tensile failures. Numerical simulation results showed that the crack initiation stress of PFCPB was reduced by the PF. The number of cracks first dropped and then gradually increased when the PF angle was enhanced, while gradually increased with the LR increased. Meanwhile, the mesoscopic AE characteristics of CPB were strongly in line with the test results. The AE events of 0 ~ 60° PFCPB experienced two slow rising periods and rapid rising periods. The temporal and spatial distribution characteristics of AE corresponded to the crack evolution trend. The PF was prone to stress concentration, especially at the tip and upper and lower surfaces of 0 ~ 45° PF, resulting in rapid crack initiation and reducing the energy storage limit and mechanical behavior of 0 ~ 45° PFCPB. The increasing LR (within a certain range) was in favor of improving the mechanical behavior of the filling body. The research results can provide a basic reference for the stability evaluation of the filling body with initial defects.