Broadband Organic Ternary Bulk Heterojunctions Photodetector Based on Non-Fullerene Acceptor with Enhanced...

Both flat-spectrum responsivity and high external quantum efficiency (EQE) of bulk heterojunction organic photodetectors (BHJ OPDs) are greatly in demand and still challenging to realize from the ultraviolet (UV) to near-infrared (NIR) regions. In this article, conjugated polymer donor poly(3-hexylthiophene) (P3HT) and PTB7-Th are blended with a low band gap nonfullerene acceptor (NFA) IEICO-4F to form a ternary BHJ active layer, thereby forming a BHJ OPD with a broadband responsivity spectrum from UV to visible light to NIR region (200-1100 nm). Under 6 V voltage and in the range from 280 to 810 nm, the ternary BHJ OPD shows a relatively flat responsivity spectrum, and the highest responsivity is 1.348 A/W, which is 1.34 times that of the binary BHJ OPD. Specifically, the ternary BHJ OPD achieved the highest EQE at 285 nm and as high as 449.31%. In addition, the ternary OPD detectivity (D*) is 2.65 times that of the binary BHJ OPD. Therefore, ternary BHJ as an active layer provides an effective method to develop BHJ OPDs with an expanded response range, higher responsivity, improved EQE, and broadband spectrum with flat spectral response from the UV to NIR region.