Diffusion-Mediated Morphological Transformation in Bifunctional Mn₂O₃/CuO-(VO)₃(PO₄)₂·6H₂O for Enhanced...

A strategical approach for morphological transformation and heterojunction formation was utilized to suppress the shortcomings of uni-metal oxide electrocatalysts and enhance their bifunctionality. In situ generation of copper oxide (CuO) over the surface of manganese oxide (Mn₂O₃) resulted in a morphological transformation from solid spheres to hollow spherical structures due to the ion-exchange diffusion (Kirkendall effect) of Cu ions into Mn₂O₃ particles. This hollowness resulted in the advancement of the bifunctional electrocatalytic behavior of Mn₂O₃/CuO (overpotential (η₁₀) of 280 mV for an OER and 310 mV for an HER at a current density of 10 mA/cm²) by virtue of increased exposed surface active sites aiding the adsorption of water molecules on the surface. The increased electrochemical active surface area (ECSA/C_dl = 34 mF/cm²) and reduced charge transfer resistance resulted in the formation of Mn₂O₃/CuO hollow spheres to achieve an approximately threefold enhancement in the turnover frequency (TOF) compared to the bare Mn₂O₃. The electrocatalytic efficiency of Mn₂O₃/CuO was further enhanced by virtue of the faster charge transfer coefficient of two-dimensional (2D) vanadyl phosphate hexahydrate (VOP) sheets deposited over its surface. This boosted the overall water splitting with attained overpotential (η₁₀) values of 190 and 220 mV with Tafel slopes of 60 and 105 mV/decade for an OER and HER, respectively. The morphological transformation and formation of an n-p heterojunction between Mn₂O₃ and CuO based on their work function (φ) values evaluated from the density functional theory (DFT) calculation and the effect of the VOP overlayer for faster reaction kinetics at the electrolyte interface resulted in an ∼10-fold increment in TOF values compared to the bare counterpart.