Waste toner-derived porous iron oxide pigments with enhanced catalytic degradation property

'Wealth from Waste' is an emerging concept, since it leads an effective waste treatment and waste recyclability. On the other hand, cost effective production iron oxide (IO) nanomaterials is still needed to develop, owing to their wide applications. Herein, we proposed a simple direct calcination method to prepare porous IO (Fe₃O₄ and Fe₂O₃) nanomaterials from waste toner powder. Characterization techniques reveal that a structural change happened from Fe₃O₄ to γ-Fe₂O₃ and γ-Fe₂O₃ to α-Fe₂O₃ at the calcination temperature of 500 °C and 700 °C respectively. Consequently, optical (band gap) and magnetic parameters of IO samples were significantly varied. The pigment characteristics of the IO samples were evaluated using Commission Internationale de l'Eclairage (CIE) analysis. IO900 sample has shown good brown-red coloration (L* = 43.11, a* = 13.26 and b* = 5.69) and it also exhibited good stability in acidic and basic conditions. Practical applicability of IO pigments were also tested by mixing with plaster of paris (PP) powder. Further, porous IO samples were also used as catalysts in the reductive degradation of methyl orange (MO) dye in presence of excess sodium borohydride (NaBH₄). IO, prepared at 900 °C exhibited ∼99.9% reduction efficiency within 40 min. Recycling experiments indicated that IO900 possess good stability up to seven cycles. The present porous IO samples will become potential in pigment and environmental remediation.